The Optimization Tests of Robiniapseudoacacia/ Wastepaper Composite Particle Board

Fang DING, Qiuhui ZHANG, Zhigao LIU

Abstract


This article research that how the single-factor variable affect the MOR and thickness swelling rate of the particle board via orthogonal experiments. The optimum condition of the maximum MOR value is 20% resin content, 120℃ hot pressing temperatures, 10 minutes hot pressing time and the proportion of Robiniapseudoacacia/ wastepaper(w/w) is 1/1. Under this situation the MOR of composite particle board is 15.4MPa and the thickness swelling rate is 16.37%. The order of the factors from majority to minority influence is resin content > proportion of Robiniapseudoacacia/ wastepaper (w/w) > hot pressing time> hot pressing temperatures.
Key words: Robiniapseudoacacia; Wastepaper; Orthogonal Experiments; MOR

Keywords


Robiniapseudoacacia; Wastepaper; Orthogonal Experiments; MOR

References


China Paper Association. (2007). The annual report of China's paper industry in 2006, China Pulp & Paper Industry, 28 (6), 5-15.

SONG, HU.(2005). Research on Hornification of Recycled Fiber, South West Pulp and Paper, 34(4), 28-31

SHAO Suying, HU Kaitang. (2002). Hornification of Recycled Fiber, China Pulp and Paper, 2, 57-60




DOI: http://dx.doi.org/10.3968%2Fj.ans.1715787020110401.005

Refbacks

  • There are currently no refbacks.


Reminder

If you have already registered in Journal A and plan to submit article(s) to Journal B, please click the CATEGORIES, or JOURNALS A-Z on the right side of the "HOME".

We only use the following emails to deal with issues about paper acceptance, payment and submission of electronic versions of our journals to databases:
caooc@hotmail.com; office@cscanada.net; office@cscanada.org
ans@cscanada.net;ans@cscanada.org

Copyright © Canadian Research & Development Centre of Sciences and Cultures (CRDCSC)
Address:758, 77e AV, Laval, Quebec, H7V 4A8, Canada

Telephone: 1-514-558 6138
Http://www.cscanada.net; Http://www.cscanada.org
E-mail:caooc@hotmail.com; office@cscanada.net